| 特性級別 | 標(biāo)準(zhǔn)級||| |
| 牌號 | T30S |
| 加工級別 | 注墮級||| |
| 品名 | PP T30S 延安延長石油 |
| 廠家(產(chǎn)地) | 沙特APPC |
| 用途級別 | 通用級|||板材級||| |
PP 延安延長 T30S
PP T30S 延安延長石油
聚丙烯均聚物
Nizhnekamskneftekhim Inc.
產(chǎn)品說明
Product obtained by polymerization of propylene in presence of complex organic metal catalysts.
It incorporates increased long-term thermal stability, thermaloxidative degradation resistance when PP is produced, processed and PP-made articles are exploited.
Application: film thread for bags, packing rope and string.
Technical requirements: TU 2211-136-05766801-2006
PP 延安延長 T30S
PP T30S 延安延長石油
| 基本信息 | |
|---|---|
| 特性 |
|
| 形式 |
|
| 用途 |
|
| 物理性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 密度 | 0.900 | g/cm3 | |
| 表觀密度 | 0.48 到 0.52 | g/cm3 | |
| 熔流率（熔體流動速率）(230°C/2.16 kg) | 2.9 到 3.5 | g/10 min | ASTM D1238 |
| 灰份含量 | 0.025 到 0.050 | % | |
| 凝膠含量 1 | |||
> 200.0 μm | 500 | pcs/m2 | |
0.700 到 1.50 mm | 50.0 | pcs/m2 | |
1.50 到 2.50 mm | 3.00 | pcs/m2 | |
> 2.50 mm | 0.00 | pcs/m2 | |
| 硬度 | 額定值 | 單位制 | 測試方法 |
| 洛氏硬度(R 級) | 82 到 95 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
|---|---|---|---|
| 抗張強度(屈服) | 34.0 | MPa | ASTM D638 |
| 伸長率(屈服) | 10 | % | ASTM D638 |
| 彎曲模量 | 1400 | MPa | ASTM D790 |
| 熱性能 | 額定值 | 單位制 | |
|---|---|---|---|
| 維卡軟化溫度 2 | 150 到 154 | °C |
| 補充信息 | 額定值 | 單位制 | |
|---|---|---|---|
| Thermal Creep Temperature 3 | 90 到 96 | °C | |
| Thermal-oxidative Deterioration(150°C) | 15.0 | day |
| 備注 | |
|---|---|
| 1. | p.4.8TU 2211-136-05766801-2006 |
| 2. | in liquid medium under force 10 H |
| 3. | at load 0.46 H/mm2 |
PP 延安延長 T30S
PP T30S 延安延長石油